實驗室臺柜
環(huán)氧樹脂板耐腐蝕性能
|
無機酸 |
黑色 |
鉑金灰 |
珍珠白 |
叢林綠 |
太平洋藍 |
|
鉻酸 (CrO3) 40% |
2 |
2 |
2 |
1 |
3 |
|
鹽酸 (HCl) 10% |
1 |
1 |
1 |
1 |
1 |
|
鹽酸 (HCl) 37% |
1 |
1 |
1 |
1 |
1 |
|
硝酸 (HNO3) 40% |
1 |
1 |
1 |
1 |
1 |
|
硝酸 (HNO3) 70% |
2 |
2 |
2 |
2 |
2 |
|
硫酸 (H2SO4) 40% |
1 |
1 |
1 |
1 |
1 |
|
硫酸 (H2SO4) 96% |
5 |
5 |
5 |
5 |
5 |
|
有機酸 |
|||||
|
乙酸 (CH3CO2H) -5% |
2 |
2 |
2 |
1 |
1 |
|
乙酸(CH3CO2H) –冰醋酸 |
2 |
1 |
1 |
1 |
1 |
|
檸檬酸 (C6H8O7) -1% |
1 |
1 |
1 |
1 |
1 |
|
油酸 (C18H34O2) |
1 |
1 |
1 |
1 |
1 |
|
石炭酸(C6H5OH) -5% |
1 |
1 |
1 |
1 |
1 |
|
堿性溶劑 |
|||||
|
氫氧化銨 (NH4OH) -10% |
1 |
1 |
1 |
1 |
1 |
|
氫氧化鉀 (KOH) -15% |
1 |
1 |
1 |
1 |
1 |
|
碳酸鈉 (Na2CO3) -20% |
1 |
1 |
1 |
1 |
1 |
|
氫氧化鈉 (NaOH) -60% |
1 |
1 |
2 |
1 |
2 |
|
次氯酸鈉 (NaOCl) -4% |
1 |
1 |
1 |
1 |
1 |
|
有機化合物 |
|||||
|
苯胺(C6H5NH2) |
2 |
1 |
1 |
2 |
1 |
|
礦物油 |
1 |
1 |
1 |
1 |
1 |
|
橄欖油 |
1 |
1 |
1 |
1 |
1 |
|
肥皂 -1% |
1 |
1 |
1 |
1 |
1 |
|
變壓器油 |
1 |
1 |
1 |
1 |
1 |
|
松節(jié)油 |
2 |
1 |
1 |
1 |
2 |
| 有機溶劑 | |||||
| 丙酮 (CH3COCH3) |
3
|
2
|
2
|
2
|
2
|
| 苯 (C6H6) |
2
|
2
|
2
|
2
|
2
|
| 四氯化碳 (CCl4) |
1
|
1
|
1
|
1
|
1
|
| 二乙基(CH3CH2OCH2CH3) |
1
|
1
|
1
|
1
|
1
|
| DMF(HCON[CH3]2) |
1
|
1
|
1
|
1
|
1
|
| 乙酸乙酯 (CH3CO2C2H5) |
2
|
2
|
2
|
2
|
2
|
| 乙醇 (CH3CH2OH) -95% |
1
|
1
|
1
|
2
|
1
|
| 二氯化乙(ClCH2CH2Cl) |
1
|
1
|
1
|
1
|
1
|
| 庚烷(CH3[CH2]5CH3) |
1
|
1
|
1
|
1
|
1
|
| 異辛烷 (C8H18) |
1
|
1
|
1
|
1
|
1
|
| 煤油 |
1
|
1
|
2
|
1
|
1
|
| 甲醇(CH3OH) |
1
|
1
|
1
|
1
|
1
|
測試方法：
方法A： 針對揮發(fā)性化學試劑。采用預浸過化學試劑的棉球，放置于容積為1盎司的瓶中（10mm x 75mm的試管或類似的容器）。 該瓶倒置于所測試的材料表面持續(xù)24小時。測試溫度為：23o +/- 2oC (73o +/- 4oF)。這種方法適用于有機試劑。
Method A – for volatile chemicals. A cotton ball, saturated with the test chemical, was placed in a one ounce bottle (10mm x 75mm test tube or similar container). The container was inverted on the test material surface for a period of 24 hours. Temperature of test: 23o +/- 2oC (73o +/- 4oF). This method was used for the organic solvents.
方法 B： 針對不揮發(fā)的化學試劑。將5滴（1/4cc）化學試劑置于所測試材料的表面。然后用25mm的表面皿覆蓋于化學試劑上持續(xù)24小時。測試溫度為：23o +/- 2oC (73o +/- 4oF)。這種方法適用于所列示的除溶劑外的其他試劑。
Method B – for non-volatile chemicals. Five drops (1/4cc) of the test chemical were placed on the test material surface. The chemical was covered with a watch glass (25mm) for a period of 24 hours. Temperature of test: 23o +/- 2oC (73o +/- 4oF). This method was used for all chemicals listed below other than the solvents.
評估：在持續(xù)放置24小時后，測試的區(qū)域先用水清洗，再用清潔劑清洗，然后使用異丙醇清洗。最后用蒸餾水漂洗，用布擦干。
Evaluation – After 24 hour exposure, exposed areas were washed with water , then a detergent solution and finally with isopropyl alcohol, rinsed with distilled water and dried with a cloth.
測試評分
1 – 無影響：在材料表面無可察覺的改變。
2 – 優(yōu) 秀： 在顏色與光澤方面有輕微可察覺的改變，但對材料表面的功能與壽命無影響。
3 – 較 好： 顏色與光澤有清晰可辨的改變，但對材料表面的功能與壽命無重要影響。
4 – 一 般： 由于變色或腐蝕，外觀有不雅改變。如果延長測試時間，有可能造成功能的損毀。
5 – 失 ?。?表面出現(xiàn)斑痕、坑凹或侵蝕，明顯且重要的材料損毀。
1 – No Effect: No detectable change in the material surface.
2 – Excellent: Slight detectable change in color or gloss but no change in function or life of the surface.
3 – Good: A clearly discernable change in color or gloss but no significant impairment of surface life or function.
4 – Fair: Objectionable change in appearance due to discoloration or etch, possibly resulting in deterioration of function over an extended period of time.
5 – Failure: Pitting, cratering, or erosion of the surface. Obvious and significant deterioration.
物理性能測試：
|
物理性能
|
測試標準
|
英制單位
|
國際單位
|
|
抗壓強度
|
ASTMD695
|
38,500 psi
|
265 MPa
|
|
抗彎強度
|
ASTMD790
|
17,000 psi
|
117 MPa
|
|
抗拉強度
|
ASTMD638
|
10,500 psi
|
72 MPa
|
|
密度
|
ASTMD792
|
125.5 Ibs/ft3
|
2.01 g/cm3
|
|
洛氏M硬度
|
ASTMD785
|
110
|
110
|
|
熱變形溫度
|
ASTMD648
|
334F
|
168C
|
|
熱膨脹系數(shù)
|
ASTMD696
|
1.31*10-5 in./ F
|
2.35*10-5 mm/C
|
|
抗火性
|
ASTMD635
|
不可燃
|
不可燃
|
|
吸水性
|
ASTMD570
|
0.008%
|
0.008%
|
抗高溫性能測試
測試A：陶瓷坩堝。將置于所測試材料表面的陶瓷坩堝，加熱至暗紅色然后讓其冷卻，溫度降至室溫。
Test A: porcelain Crucible – A porcelain crucible was heated to a dull red color, placed on the test material, and allowed to cool to ambient temperature.
觀測結果：無起泡，裂縫或任何表面變形。
Observation: No blisters, no cracks nor any surface deformations were observed on the work surface.
測試B：煤氣噴燈。將一個3/8〞 的煤氣噴燈調到穩(wěn)定的火焰使其藍色錐形內焰為1-1/2〞，然后，將煤氣噴燈翻轉，是火焰接觸所測試的材料5分鐘。
Test B: Bunsen Burner A 3/8〞Bunsen burner was adjusted to a quiet flame with a 1-1/2〞inner blue cone and then overturned on the test material, exposing material to the flame for 5 minutes.
觀測結果：無起泡或裂縫。
Observation: No blisters nor cracks were detected on the exposed work surface.